PP Fiber Monofilament 110F
Function:
Resist to shrink & crack
Increase seepage resistance
Increase friction resistance
Increase freezing & thawing resistance
Improve tendons protection
Replace steel net (using in plastering)
Prevent mortar split and crackle expansion
Increase impact resistance and peeling resistance
Feature:
1. Easy to be dispersed in mortar or concrete and no agglomeration,
it can guarantee the property of crack resistance effectively
2. No need to change the proportion of mortar, just put the fibers
into the mortar mixture and stir for a moment after adding water.
3. It with fine economic property: The equivalent diameter of the
fiber is only φ 30um, so the ratio of diameter and surface area is
high and on the basis of crack resistance, it can reduce the amount
(to about 0.6kg/m 3 ).
4. Easy to plaster: As the great number of thin fibers spread into
mortar evenly, the plastering is much easily and this can improve
the binding strength between surface and base.
5. It with stable chemical property, strong acid &alkali
resistance, and can be used in any engineering projects.
Suitable Project:
A). Be suitable for the water–proof layer, floor, inner &outer
wall of industrial and civil construction.
B). Increase cracking resistance on the surface of industrial
workshop, warehouse and parking lot.
C). Increase cracking & seepage resistance of the ground in
natatorium, swimming pool, pond and ditch.
D). Be suitable for any mortar projects and fine aggregate concrete
projects
Specification:
| Index | Standard |
| Raw Material | 100% virgin Polypropylene |
| Fiber Type | Monofilament (Microfiber) |
| Density(g/cm3) | 0.91 |
| Fiber Diameter (um) | 30+/-5 |
| Tensile Strength (Mpa) | 500 min. |
| Elastic Modulus (Mpa) | |
| Melting Point(℃) | 160—170 |
| Length (mm) | 6, 12, 18... |
| Crack Elongation (%) | 15-20 |
| Acid &Alkali Resistance | Strong |
Applying Instruction:
A). Compound Amount. To resist the common cracks on surfaces,
0.6kg/m3 fibers
to cement paint is enough, and for reinforced application
0.9-1kg/m3 is enough.
B). Stirring requirement. The proportion of cement, sand and
aggregate is no need to
be changed. Put cement, aggregate, additive and fiber together,
then stir after adding
enough water (Do not stir without water!) and time for stirring can
be prolonged for
2~3 minutes in order to make the compound mix completely